Physical Properties

Classic Rubber Graphite

Property	ASTM Method	Value or Rating
Density	DIN 53479	1.6 kg/dm
Water Absorption	DIN 53472	0,18% (volume) 0,25% (mass)
Coefficient of Expansion	DIN 52328	1x10^-5.K-1 (6x10^-6 in/in/ °F)
Coefficient of Friction		0,12 dynamic (dry, against stainless steel)
Hardness		78 Shore D
Max Operation Temperature		120°C (250°F)

Coldflex

Property	ASTM Method	Value or Rating
Density	DIN 53479	1.6 kg/dm
Water Absorption	DIN 53472	0,18% (volume) 0,25% (mass)
Coefficient of Expansion	E831-00	3x10^-5.K-1 (19x10^-6 in/in/ °F)
Coefficient of Friction		0,12 dynamic (dry, against stainless steel)
Hardness		63 Shore D
Max Operation Temperature		120°C (250°F)

Blue Vincon Air Load Tubing

Property	ASTM Method	Value or Rating
Durometer Hardness (Shore A), 15s	D2240-91	55
Tensile Strength, psi (MPa)	D412-92	1,831 (12.6)
Ultimate Elongation, %	D412-92	406
Tensile Set (@ 75% of Ultimate Elongation), %	D412-92	77
Tear Resistance, lb-f/inch (kN/m)	D1004-93	159 (27.8)
Compression Set Constant Deflection, % @ 158°F (70°C) for 22 hours	D395-89 Method B	65
Brittle Temperature, °F (°C)	D746-79	-50 (-45)
Specific Gravity	D792-91	1.180
Water Absorption, % 24 hrs at 73°F (23°C)	D570-81	0.16
Maximum Recommended Operating Temperature °F (°C)	-	165 (74)
Toxicity	-	Non-Toxic
Color	-	Blue
Unless otherwise noted, all tests were conducted at room temperature (73°F). Values shown were determined on 0.075" thick extruded strip or 0.075" thick molded ASTM plaques or molded ASTM durometer buttons.

RELATIVE CHEMICAL RESISTANCE PROPERTIES*
Acids			Bases			Salts	Alcohols	Ketones
conc.	med.	weak	conc.	med.	weak
F	E	E	E	E	E	E	F	U
E = Excellent F = Fair U = Unsatisfactory * All tests conducted at room temperatures.

Black Neoprene Air Load Tubing

Unaged Physical Properties	ASTM Method	Requirements	Test	Pass/Fail
Tensile Strength, Mpa (PSI)	D412	1450	1644	Pass
Elongation at Break		250	300	Pass
Hardness, Type A, +/-5	D2240	50	52	Pass
Oven Aged Physical Properties	ASTM Method	Requirements	Test	Pass/Fail
70 Hours @ 212°F (100°C)	D573
Tensile Strength, % Change Max.		-13	+2.0	Pass
Elongation, % Cange Max.		-40	-15.0	Pass
Hardness, Type A, Pt. Change Max.		+15	+6	Pass
Compression Set Max %	ASTM Method	Requirements	Test	Pass/Fail
22 Hours @ 212°F (100°C)		35%	32.60	Pass
Low Temperature	ASTM Method	Requirements	Test	Pass/Fail
Max. C, Determine Actual Temp.		-55°C	5 of 5	Pass
Slab Cured: 20 Min. @ 320°F, Button Cured: 20 Min. @ 320°F

UHMW - CW1000 (Color: Natural / Black)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	930	ASTM D-792	lbs/ft³	58.01
Tensile Strength (Yield)	DIN 53455	MPa	24	ASTM D-638	psi	3050
Elongation at Yield	DIN ISO / R 527	%	15	ASTM D-638	%	15
Tensile Break	DIN 53455	MPa	40	ASTM D-638	psi	5800
Elongation at Break	DIN ISO / R 527	%	325	ASTM D-638	%	325
Tensile Modulus	DIN ISO / R 527	MPa	760	ASTM D-638	psi	120000
Charpy / Izod Impact	DIN 53453	kJ/m²	110	ASTM D-4020	ft-lbs/in²	26
Hardness @ 20 °C	DIN 53505	Type D	65 - 68	ASTM D-2240	Type D	65 - 68
Static Friction		Unitless	0.12	ASTM D-1894	Unitless	0.12
Dynamic Friction		Unitless	0.071	ASTM D-1894	Unitless	0.071
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.0002	ASTM D-696	°F^-1	0.00011
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	82		°F	180
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

UHMW - CW2000 (Color: Dark Blue)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	933	ASTM D-792	lbs/ft³	58.2
Tensile Strength (Yield)	DIN 53455	MPa	22.1	ASTM D-638	psi	3200
Elongation at Yield	DIN ISO / R 527	%	15	ASTM D-638	%	15
Tensile Break	DIN 53455	MPa	29	ASTM D-638	psi	4200
Elongation at Break	DIN ISO / R 527	%	158	ASTM D-638	%	158
Tensile Modulus	DIN ISO / R 527	MPa	896	ASTM D-638	psi	130000
Izod Impact	DIN 53453	kJ/m²	63	ASTM D-4020	ft-lbs/in²	30
Hardness @ 20 °C	DIN 53505	Type D	65 - 68	ASTM D-2240	Type D	65 - 68
Static Friction		Unitless	0.12	ASTM D-1894	Unitless	0.12
Dynamic Friction		Unitless	0.072	ASTM D-1894	Unitless	0.072
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.00018	ASTM D-696	°F^-1	0.00011
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	82		°F	180
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

UHMW - CW5000 (Color: Light Blue / Green)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	977	ASTM D-792	lbs/ft³	60.2
Tensile Strength (Yield)	DIN 53455	MPa	21	ASTM D-638	psi	2800
Elongation at Yield	DIN ISO / R 527	%	12	ASTM D-638	%	12
Tensile Break	DIN 53455	MPa	31	ASTM D-638	psi	3800
Elongation at Break	DIN ISO / R 527	%	325	ASTM D-638	%	325
Tensile Modulus	DIN ISO / R 527	MPa	800	ASTM D-638	psi	130970
Charpy / Izod Impact	DIN 53453	kJ/m²	105	ASTM D-4020	ft-lbs/in²	50
Hardness @ 20 °C	DIN 53505	Type D	65 - 68	ASTM D-2240	Type D	65 - 68
Static Friction		Unitless	0.12	ASTM D-1894	Unitless	0.12
Dynamic Friction		Unitless	0.074	ASTM D-1894	Unitless	0.074
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.00018	ASTM D-696	°F^-1	0.00011
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	82		°F	180
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

UHMW - CW6000 (Color: Dark Grey)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	972	ASTM D-792	lbs/ft³	59.56
Tensile Strength (Yield)	DIN 53455	MPa	21	ASTM D-638	psi	2800
Elongation at Yield	DIN ISO / R 527	%	15	ASTM D-638	%	15
Tensile Break	DIN 53455	MPa	35.7	ASTM D-638	psi	5280
Elongation at Break	DIN ISO / R 527	%	325	ASTM D-638	%	325
Tensile Modulus	DIN ISO / R 527	MPa	675	ASTM D-638	psi	101900
Charpy / Izod Impact	DIN 53453	kJ/m²	100	ASTM D-4020	ft-lbs/in²	24
Hardness @ 20 °C	DIN 53505	Type D	65 - 68	ASTM D-2240	Type D	65 - 68
Static Friction		Unitless	0.13	ASTM D-1894	Unitless	0.13
Dynamic Friction		Unitless	0.119	ASTM D-1894	Unitless	0.119
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.00018	ASTM D-696	°F^-1	0.00011
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	90		°F	194
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

UHMW - CW6500 (Color: Light Grey)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	951	ASTM D-792	lbs/ft³	58.9
Tensile Strength (Yield)	DIN 53455	MPa	21.8	ASTM D-638	psi	3017
Elongation at Yield	DIN ISO / R 527	%	12	ASTM D-638	%	12
Tensile Break	DIN 53455	MPa	32	ASTM D-638	psi	4105
Elongation at Break	DIN ISO / R 527	%	200	ASTM D-638	%	200
Tensile Modulus	DIN ISO / R 527	MPa	675	ASTM D-638	psi	101900
Izod Impact	DIN 53453	kJ/m²	na	ASTM D-4020	ft-lbs/in²	na
Hardness @ 20 °C	DIN 53505	Type D	65 - 68	ASTM D-2240	Type D	65 - 68
Static Friction		Unitless	0.14	ASTM D-1894	Unitless	0.14
Dynamic Friction		Unitless	0.12	ASTM D-1894	Unitless	0.12
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.00018	ASTM D-696	°F^-1	0.00011
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	90		°F	194
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

UHMW - CW7000 (Color: Pearl White)

Property	Method	SI Unit	SI Value	Method	English Unit	English Value
Molecular weight (average molar mass)		g/mol	> 9 mill
Density	DIN 53479	kg/m³	1000	ASTM D-792	lbs/ft³	63.02
Tensile Strength (Yield)	DIN 53455	MPa	> 19	ASTM D-638	psi	> 2700
Elongation at Yield	DIN ISO / R 527	%	12	ASTM D-638	%	12
Elongation at Break	DIN ISO / R 527	%	> 100	ASTM D-638	%	> 100
Tensile Modulus	DIN ISO / R 527	MPa	675	ASTM D-638	psi	101900
Charpy / Izod Impact	DIN 53453	kJ/m²	> 128	ASTM D-4020	ft-lbs/in²	16.2
Hardness @ 20 °C	DIN 53505	Type D	66 - 68	ASTM D-2240	Type D	66 - 68
Static Friction		Unitless	0.17	ASTM D-1894	Unitless	0.17
Dynamic Friction		Unitless	0.13	ASTM D-1894	Unitless	0.13
Coefficient of Thermal Exp.	DIN 53752	°C^-1	0.00017	ASTM D-696	°F^-1	0.0001
Melt Point	DTA	°C	130 - 143	ASTM D-3417	°F	278 - 289
Maximum Operating Temp.		°C	90		°F	194
Water Absorption		%	nil		%	nil
* Values are averages and are not specifications. ** ASTM test methods are under current procedures.

Ceramic

			Alumina	Silicon Nitride	Silicon Carbide
MATERIAL CODE	CONDITION	UNITS	99.5AL	SN220	SC2000
BULK DENSITY		g/cc	3.8	3.2	3.1
WATER ABSORPTION		%	0	0	0
HARDNESS	Hv	GPa	16.1	13.7	26.0
HARDNESS	Hv	kg/mm²	1650	1400	2650
FLEXURAL STRENGTH	Room Temp.	MPa	320	550	400
	1000 °C	MPa		496	-
	1400 °C	MPa	-	-	-
FRACTURE TOUGHNESS	Room Temp.	MPam^1/2	3.5	5.7	4.0
YOUNG'S MODULUS		GPa	363	291	410
POISSON'S RATIO	Room Temp.		0.23	0.28	0.14
THERMAL EXPANSION	40-400 °C	x10^-6/ °C	7.1	2.5	4
THERMAL CONDUCTIVITY	Room Temp.	W/m*K	32	20	103
THERMAL CONDUCTIVITY	1200 °C	W/m*K	-	13	-
SPECIFIC HEAT	Room Temp.	J/g*K	0.75	0.66	0.67
HEAT SHOCK RESISTANCE		°C	200	550	350
Note: The values are typical material properties and may vary according to the product's configuration and manufacturing process.

North America +1 (404) 842-0012 / Europe +46 (0) 554-68 98 20 / Asia +86 (512) 5777-7691
info@coldwaterseals.com